Experimental Investigation and Thermodynamic Modelling of Ag–In–Pd Ternary System

A. V. Khoroshilov; Хорошилов А. В.; V. N. Kuznetsov; Кузнецов В. Н.; A. S. Pavlenko; Павленко А. С.; E. A. Ptashkina; Пташкина Е. А.; G. P. Zhmurko; Жмурко Г. П.; E. G. Kabanova; Кабанова Е. Г.; M. A. Kareva; Карева М. А.

doi:10.31857/S0044453723010235

Experimental Investigation and Thermodynamic Modelling of Ag–In–Pd Ternary System

作者: Khoroshilov A.V.¹, Kuznetsov V.N.², Pavlenko A.S.², Ptashkina E.A.², Zhmurko G.P.³, Kabanova E.G.², Kareva M.A.²
隶属关系:
1. Institute of General and Inorganic Chemistry
2. Chemical Faculty, Moscow State University
3. Institute of General and Inorganic Chemistry, Russian Academy of Sciences
期: 卷 97, 编号 1 (2023)
页面: 46-54
栏目: ХИМИЧЕСКАЯ ТЕРМОДИНАМИКА И ТЕРМОХИМИЯ
##submission.dateSubmitted##: 27.02.2025
##submission.datePublished##: 01.01.2023
URL: https://freezetech.ru/0044-4537/article/view/668867
DOI: https://doi.org/10.31857/S0044453723010235
EDN: https://elibrary.ru/BCRZNU
ID: 668867

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细

Phase equilibria in Ag–In–Pd ternary system were studied using Scanning electron microscopy, Energy-dispersive X-ray spectroscopy (EDX) and X-Ray diffraction method (XRD). The solubilities of the third components in Ag–In and In–Pd binary phases were established, as well as composition ranges (from 4 to 17.5 at % Ag at 25 at % In) and crystal structure of τ ternary compound (Al3Ti). New thermodynamic assessment of Ag–In–Pd ternary system was performed, basing on the published experimental data and those obtained in the present work. Good agreement was achieved between the calculation results and the experimental data on phase equilibria and thermodynamic properties of the phases. The results of the calculation reproduce well experimental DTA/DSC data of three samples (the data were not included into the optimization). This additionally supports the correctness of the obtained thermodynamic description.

关键词

palladium alloys, phase equilibria, thermodynamic modelling

参考

Shin H.-J., Kwon Y.H., Seol H.-J. // J. Mech. Behav. Biomed. Mater. 2020. V. 107. P. 103728. https://doi.org/10.1016/j.jmbbm.2020.103728
Zemanová A., Semenova O., Kroupa A. et al. // Monatsch. Chem. 2005. V. 136. № 11. P. 1931.https://doi.org/10.1007/s00706-005-0384-x
Zemanová A., Semenova O., Kroupa A. et al. // Intermetallics. 2007. V.15. № 1. P. 77. https://doi.org/10.1016/j.intermet.2006.03.002
Luef C., Flandorfer H., Ipser H. // Metall. Mater. Trans. A. 2005. V. 36. № 5. P. 1273. https://doi.org/10.1007/s11661-005-0219-8
Garzeł G., Zabdyr L.A. // Rare Met. 2006. V. 25. № 5. P. 587. https://doi.org/10.1016/S1001-0521(06)60104-6
STOE WinXPow, version 2.24. Darmstadt электронный ресурс. – Software package (10.2 Mb). Germany: STOE & Cie GmbH; 2009.
Thermo-Calc®-Academic (Version 2022а) электронный ресурс. – Software package (235 Mb). – Stockholm: Thermo-Calc® Software AB.; 2022.
Saunders N., Miodovnik A.P. CALPHAD (Calculation of Phase Diagrams): A comprehensive guide. London: Pergamon, 1998. 479 p.
Kohlmann H., Ritter C. // Z. Anorg. Allg. Chem. 2009. V. 635. P. 1573. https://doi.org/10.1002/zaac.200900053
Bhan S., Schubert K. // J. Less-Common Met. 1969. V. 17 P. 73. https://doi.org/10.1016/0022-5088(69)90038-1
Ptashkina E.A., Kabanova E.G., Kalmykov K.B. et al. // J. of Alloys Comps. 2020. V. 845. P. 156166. https://doi.org/10.1016/j.jallcom.2020.156166
Muzzillo C.P., Anderson T. // J. Mater. Sci. 2018. V. 53. № 9. P. 6893. https://doi.org/10.1007/s10853-018-1999-8
Pavlenko A.S., Kabanova E.G., Kuznetsov V.N. // Russ. J. Phys. Chem. A. 2020. V. 94. № 13. P. 2691. https://doi.org/10.1134/s0036024420130178
Jiang C., Liu Z.K. // Metall. Mater. Trans. A. 2002. V. 33. № 12. P. 3597. https://doi.org/10.1007/s11661-002-0235-x